クリンカー系セメント生産プロセスにおけるカーボンフットプリントの評価
Assessment of the Carbon Footprint in the Clinker-Based Cement Production Process (原題)
Damira Sambaeva, Chynara Jayloobaikyzy, Zarlik Maimekov, Miraida Turgunbekova, Janarbek Izakov
🤖 gxceed AI 要約
日本語
キルギスのセメント工場（Terek-Tash LLC）の原料消費データをもとに、クリンカーのモデル化学組成を構築し、炭酸カルシウムの高温分解に伴うCO・CO2の生成量を温度別に推算した研究。最大エントロピー条件下での含炭素フラグメントの濃度分布を計算し、セメント生産プロセスのカーボンフットプリントを熱力学的に評価している。既存の環境規制が業種一般の環境問題にとどまり、セメント製造の炭素負荷評価が未整備である点を指摘する。
English
Using raw-material consumption data from a Kyrgyz cement plant (Terek-Tash LLC), the authors model the chemical composition of clinker and estimate CO and CO2 formation from high-temperature limestone decomposition across temperatures. Concentration distributions of carbon-containing fragments at maximum entropy are calculated to quantify the process carbon footprint. The paper notes that existing regulations address general environmental issues but leave carbon-load assessment in cement production unaddressed.
Unofficial AI-generated summary based on the public title and abstract. Not an official translation.
📝 gxceed 編集解説 — Why this matters
日本のGX文脈において
セメントは日本のScope 1排出の主要源であり、SSBJ・有報でのセクター別排出開示やクリンカー製造の脱炭素（CCUS・代替原料）を検討する実務者にとって、プロセス由来CO2の発生メカニズムを再確認する基礎的知見を提供する。ただし規制・開示制度との接続はなく、日本の制度文脈への直接的な示唆は限定的。
In the global GX context
Cement is a hard-to-abate sector central to Scope 1 disclosure under TCFD/ISSB and to transition-finance debates on clinker decarbonization. This paper offers a process-level thermodynamic account of CO2 generation from limestone calcination, useful as background for sector-specific emissions accounting, though it does not engage with disclosure frameworks or CSRD/ISSB reporting requirements.
👥 読者別の含意
🔬研究者:セメントプロセスのCO2発生を熱力学・エントロピー論から定量化する手法の一事例として参照できる。
🏢実務担当者:クリンカー焼成由来のプロセス排出を原料・温度別に把握する際の基礎的考え方として活用可能。
🏛政策担当者:セメント業種の炭素負荷評価が規制上未整備であるという指摘は、セクター別排出規制設計の論点になり得る。
📄 Abstract（原文）
This paper analyzes the economic activities of several cement plants in the republic based on their ecological passports. It was noted that existing regulatory documents addressed the general environmental issues of individual industries, while the assessment of the carbon load in the cement production process remains open. Given these circumstances, it is emphasized that the formation of carbon-containing substances, including carbon dioxide, occurs during the high-temperature decomposition of calcium carbonate, the main raw material in cement production. Based on raw material consumption data at the Terek-Tash LLC plant (Novopokrovka village, Issyk-Ata District, Chui Region, Kyrgyzstan), a model chemical composition of cement clinker was compiled. It is emphasized that calcium oxide is not used directly in cement production, but is formed during the decomposition of limestone, meaning calcium carbonate was considered a carrier of carbon-containing substances. Accordingly, the concentration distribution of components and particles, including carbon-containing fragments formed at maximum entropy, was calculated. The established physicochemical and thermodynamic parameters of calcium carbonate degradation allowed us to determine the process direction, while the concentration distribution of various carbon-containing fragments in the gas phase revealed the total carbon footprint and the quantitative content of carbon oxides (CO, CO2) depending on temperature.
🔗 Provenance — このレコードを発見したソース
- openalex http://journals.ayu.edu.kz/index.php/ijesgt/article/view/6574first seen 2026-10-23 05:24:00 · last seen 2026-10-30 05:02:57
🔔 こうした論文の新着を逃したくない方は キーワードアラート に登録（無料・3キーワードまで）。
gxceed は公開メタデータに基づく研究支援データセットです。要約・翻訳・解説は AI 支援で生成されています。 最終的な解釈・検証は利用者が原典資料に基づいて行うことを前提とします。