EFFECT OF MULTI-WALLED CARBON NANOTUBES ON THE PROPERTIES OF LOW-DENSITY NON-AUTOCLAVED AERATED CONCRETE
低密度非オートクレーブ発泡コンクリートの特性に対する多層カーボンナノチューブの効果 (AI 翻訳)
Abbas Guvalov, Rafig Shirinov
🤖 gxceed AI 要約
日本語
本研究では、低密度（250 kg/m³）の非オートクレーブ発泡コンクリート（NAAC）の機械的特性向上のために、多層カーボンナノチューブ（MWCNT）を極微量（セメント質量比0.001〜0.005%）添加する効果を検討した。結果、最適添加量（0.001〜0.003%）で圧縮強度がB0.5クラス（≧0.5 MPa）に達し、乾燥密度が300→250 kg/m³に低下、塑性強度の発現が20〜30分早まった。これにより、断熱用途向けの機械的に信頼性の高いNAACの製造が可能となった。
English
This study investigates the effect of multi-walled carbon nanotubes (MWCNTs) on low-density non-autoclaved aerated concrete (NAAC) with a target density of 250 kg/m³. Ultralow dosages (0.001–0.005% by cement mass) improved compressive strength to Class B0.5 (≥0.5 MPa) and reduced dry density from 300 to 250 kg/m³, while accelerating plastic strength development. The approach enables production of mechanically reliable NAAC for thermal insulation.
Unofficial AI-generated summary based on the public title and abstract. Not an official translation.
📝 gxceed 編集解説 — Why this matters
日本のGX文脈において
この論文は断熱用コンクリートの改良技術であり、日本の建築物の省エネ・断熱性能向上に間接的に貢献し得る。ただし、直接的なGX政策やカーボンアカウンティングとは関連しないため、日本国内のSSBJや有報対応には直接影響しない。
In the global GX context
This paper presents a material-level improvement for thermal insulation concrete, which could indirectly contribute to building energy efficiency. However, it lacks direct connection to climate disclosure frameworks (TCFD/ISSB) or decarbonization policy.
👥 読者別の含意
🔬研究者:Materials scientists or construction engineers interested in nano-modified aerated concrete for thermal insulation.
📄 Abstract（原文）
Low-density non-autoclaved aerated concrete (NAAC) is a widely used thermal insulation material; however, its mechanical strength and structural integrity decrease significantly when the density falls below 400 kg/m³. This study investigates the effect of multiwalled carbon nanotube (MWCNT) dispersion on the formation of the porous structure and the mechanical properties of low-density nonautoclaved aerated concrete with a target density of 250 kg/m³. MWCNTs were incorporated in ultralow dosages (0.001–0.005% by mass of cement). Experimental results demonstrate that the optimum MWCNT content (0.001–0.003%) increases the compressive strength to Class B0.5 (≥0.5 MPa), reduces the dry density from 300 kg/m³ to 250 kg/m³, and accelerates the development of plastic strength by 20–30 minutes compared with the control specimens. The proposed approach enables the production of mechanically reliable nonautoclaved aerated concrete (NAAC) for thermal insulation applications.
🔗 Provenance — このレコードを発見したソース
- openalex https://doi.org/10.58225/mpmma.2026.90first seen 2026-07-22 05:01:33
🔔 こうした論文の新着を逃したくない方は キーワードアラート に登録（無料・3キーワードまで）。
gxceed は公開メタデータに基づく研究支援データセットです。要約・翻訳・解説は AI 支援で生成されています。 最終的な解釈・検証は利用者が原典資料に基づいて行うことを前提とします。