パーム油燃料灰と籾殻灰をセメント完全代替に用いたジオポリマーモルタル：グリーン建材への応用
Geopolymer-Based Mortar Utilizing Palm Oil Fuel Ash and Rice Husk Ash as Full Cement Replacement for Green Building Materials (原題)
Herlina Rahim, Salsabilla
🤖 gxceed AI 要約
日本語
OPC製造が世界のCO2排出の7〜8%を占めることを背景に、パーム油燃料灰（POFA）と籾殻灰（RHA）でセメントを完全代替したジオポリマーモルタルを検討。POFA:RHA=50:50が28日圧縮強度37.9MPa（OPC比92%）と最高性能を示し、XRD/FTIRでシリカ-richなアルカリ活性化ゲルの生成を確認した。インドネシアでの低炭素建材普及への可能性を示す。
English
Geopolymer mortar fully replacing OPC with palm oil fuel ash (POFA) and rice husk ash (RHA) was tested across five blend ratios. The 50:50 blend reached 37.9 MPa at 28 days (92% of OPC control) with 8.3% water absorption, and XRD/FTIR confirmed a silica-rich alkali-activated gel. Results support low-carbon construction materials in Indonesia.
Unofficial AI-generated summary based on the public title and abstract. Not an official translation.
📝 gxceed 編集解説 — Why this matters
日本のGX文脈において
日本では建設業のScope 3（資材調達）排出削減とグリーン建材調達が焦点となる。廃棄物由来バインダーの強度データは、建材のカーボンフットプリント算定や調達基準づくりに参考になる。
In the global GX context
As CSRD/ISSB push embodied-carbon disclosure into construction supply chains, agro-waste geopolymer binders offer a pathway to cut Scope 3 category 1 emissions from cement. The quantitative strength benchmarks help practitioners assess feasibility of OPC-free materials.
👥 読者別の含意
🔬研究者:廃棄物由来アルカリ活性化バインダーの強度・微細構造データを、低炭素セメント研究の比較基盤として活用できる。
🏢実務担当者:セメント完全代替建材の性能水準を把握し、調達・設計段階での低炭素資材採用検討に使える。
🏛政策担当者:建設資材の脱炭素化促進策やグリーン調達基準の設計において、廃棄物由来バインダーの実現可能性を示す根拠となる。
📄 Abstract（原文）
Ordinary Portland cement (OPC) production contributes approximately 7–8% of global anthropogenic carbon dioxide emissions, motivating the development of low-carbon binders from agro-industrial waste. This study investigates the mechanical, physical, and microstructural properties of geopolymer mortar using palm oil fuel ash (POFA) and rice husk ash (RHA) as complete OPC replacements. Five POFA-to-RHA mass ratios (100:0, 75:25, 50:50, 25:75, and 0:100) were activated using 12 M sodium hydroxide and sodium silicate solutions. Specimens were cured under ambient laboratory conditions and tested at 7, 14, 28, and 56 days. The 50:50 POFA-RHA blend achieved the highest 28-day compressive strength among geopolymer mixtures, reaching 37.9 MPa, equivalent to 92% of the OPC control strength of 41.2 MPa. It also exhibited a bulk density of 1930 kg/m³ and water absorption of 8.3%. X-ray diffraction and Fourier-transform infrared spectroscopy indicated alkali-activated gel formation through a Si–O–T band shift from approximately 1080 to 1000 cm⁻¹ and a broad amorphous hump. With Si/Al and Ca/Si ratios of approximately 25 and 0.07, respectively, the binder is classified as a silica-rich alkali-activated hybrid system. Overall, the 50:50 blend offers a promising approach to sustainable cement replacement and low-carbon construction materials in Indonesia.
🔗 Provenance — このレコードを発見したソース
- semanticscholar https://gpijournal.com/index.php/science/article/download/871/672first seen 2026-10-29 05:37:54 · last seen 2026-11-05 06:07:47