効率的なCO2およびCO回収に向けた、タマキビガイ殻およびココナッツ殻由来炭素におけるメチレンブルー吸着効率の特性評価と相関分析
Characterization and Correlation of Methylene Blue Adsorption Efficiency in Periwinkle and Coconut Shell-Derived Carbons for Efficient CO2 and CO Capture (原題)
Sakwe Adianimovie
🤖 gxceed AI 要約
日本語
水産廃棄物（タマキビガイ殻）と農業廃棄物（ココナッツ殻）から活性炭を調製し、メチレンブルー吸着試験で細孔特性を評価した。活性化・炭化温度と時間を変えて収率・固定炭素・吸着能を比較し、タマキビガイ殻炭が最大2.88 mg/gと高い吸着能を示した。細孔がミクロ孔からメソ孔へ移行し、CO2およびCO回収材としての可能性を示唆する。
English
Activated carbons were produced from periwinkle (aquatic) and coconut (agricultural) shell waste and characterized via methylene blue adsorption tests against IUPAC pore standards. Varying activation (400–600°C) and carbonization (500–700°C) temperatures and times, periwinkle carbon reached the highest adsorption of 2.88 mg/g. Pore evolution from microporous to mesoporous structures suggests potential for CO2 and CO capture.
Unofficial AI-generated summary based on the public title and abstract. Not an official translation.
📝 gxceed 編集解説 — Why this matters
日本のGX文脈において
日本ではCCUSやカーボンリサイクルがGX政策の柱の一つであり、廃棄物由来の低コスト吸着材開発は産業実装の観点で参考になる。ただし現段階では実験室レベルの材料評価であり、SSBJ開示や企業のGX戦略に直接結びつくものではない。
In the global GX context
This study contributes to the global CCUS materials literature by valorizing aquatic and agricultural waste into low-cost adsorbents, aligning with circular-economy and hard-to-abate sector decarbonization goals. However, it remains early-stage laboratory characterization with no direct link to disclosure frameworks such as TCFD or ISSB.
👥 読者別の含意
🔬研究者:廃棄物由来活性炭の細孔制御とCO2/CO吸着能の相関を検討する材料研究者にとって、MBATをスクリーニング指標として用いる手法の一例となる。
🏢実務担当者:CCUSやカーボンリサイクルに関わる企業にとって、低コスト吸着材の原料候補として水産・農業廃棄物の可能性を示すが、実装には実ガスでの性能検証が必要。
🏛政策担当者:廃棄物由来材料を用いたCCUS技術の初期段階の研究として、循環経済と炭素回収の政策連携を検討する際の参考資料になり得る。
📄 Abstract（原文）
Human nefarious activities, eminently contributes to the increasing concentration of greenhouse gases globally specifically CO2 levels; therefore, this study determines the adsorption capacity from activated carbons produced from aquatic (periwinkle shell) and agricultural (coconut shell) waste by employing methylene blue adsorption test (MBAT) as compared to IUPAC Standard of the products micropores and mesopores for possible carbon dioxide (CO2) and carbon monoxide (CO) capture. These wastes were activated at temperatures (400, 500, 600 0C) and carbonized at temperatures (500, 600, 700 0C) at 30 minutes intervals (30, 60 and 90). At 60 minutes of activation and carbonization temperatures (500 and 600 700 0C), recorded the highest fixed carbons and yields for coconut (48, 49 %) and periwinkle (52, 51 %) respectively. On percentage comparison moisture and ash contents for coconut (55, 29 %), periwinkle (45, 71 %) while their volatile matters was 55 and 45 %. In the subjection of products to MBAT at the same recorded time (30, 60 and 90 minutes), activation and carbonization temperatures (400, 500, 600 0C) and (500, 600, 700 0C) the adsorption capacities of coconut AC recorded 1.90, 2.68, 2.44 mg/g and periwinkle yielded 1.98, 2.88, 2.46 mg/g. The coconut AC achieved a maximum adsorption of 2.68 mg/g (48 %) and periwinkle AC demonstrated a higher peak performance of 2.88 mg/g (52 %) proving their pores evolution and IUPAC Standardization indicated transition from microporous (< 2 nm) to mesoporous (2–50 nm) structures marketing these products as possible, effective and efficient CO2 and CO captures.
🔗 Provenance — このレコードを発見したソース
- openalex https://doi.org/10.56201/ijemt.vol.12.no3.2026.pg196.210first seen 2026-09-14 04:43:35
🔔 こうした論文の新着を逃したくない方は キーワードアラート に登録（無料・3キーワードまで）。
gxceed は公開メタデータに基づく研究支援データセットです。要約・翻訳・解説は AI 支援で生成されています。 最終的な解釈・検証は利用者が原典資料に基づいて行うことを前提とします。